The investigation of dye-sensitized solar cells (DSCs) using a very thin (0.8 to 4.7 mu m) transparent photoanode based on a hierarchically nanostructured TiO2 film prepared via Plasma Assisted Supersonic Jet Deposition (PA-SJD), in combination with the DSC benchmark photosensitizer N719, is presented. The cell photovoltages (nearly 0.8 V) and the amount of adsorbed dye and photocurrent densities, normalized over the film thickness, are higher than those of DSCs prepared with thicker (9 mu m) conventional screen-printed TiO2 films. A record efficiency value of 5.7% (standard AM 1.5G solar irradiation) for very thin nanostructured titania photoanodes is obtained with a 2 mm PA-SJD TiO2 film. Electrochemical impedance spectroscopy shows that PA-SJD devices are endowed with higher charge recombination resistance (lower recombination losses) and electron lifetimes compared to conventional nanocrystalline films

Trifiletti, V., Ruffo, R., Turrini, C., Tassetti, D., Rocera, R., Di Fonzo, F., et al. (2013). Dye-sensitized solar cells containing plasma jet deposited hierarchically nanostructured TiO2 thin photoanodes. JOURNAL OF MATERIALS CHEMISTRY. A, 1(38), 11665-11673 [10.1039/c3ta11485f].

Dye-sensitized solar cells containing plasma jet deposited hierarchically nanostructured TiO2 thin photoanodes

TRIFILETTI, VANIRA;RUFFO, RICCARDO;TASSETTI, DARIO;RICCARDI, CLAUDIA;ABBOTTO, ALESSANDRO
2013

Abstract

The investigation of dye-sensitized solar cells (DSCs) using a very thin (0.8 to 4.7 mu m) transparent photoanode based on a hierarchically nanostructured TiO2 film prepared via Plasma Assisted Supersonic Jet Deposition (PA-SJD), in combination with the DSC benchmark photosensitizer N719, is presented. The cell photovoltages (nearly 0.8 V) and the amount of adsorbed dye and photocurrent densities, normalized over the film thickness, are higher than those of DSCs prepared with thicker (9 mu m) conventional screen-printed TiO2 films. A record efficiency value of 5.7% (standard AM 1.5G solar irradiation) for very thin nanostructured titania photoanodes is obtained with a 2 mm PA-SJD TiO2 film. Electrochemical impedance spectroscopy shows that PA-SJD devices are endowed with higher charge recombination resistance (lower recombination losses) and electron lifetimes compared to conventional nanocrystalline films
Articolo in rivista - Articolo scientifico
plasma jet, nanostructures, solar cells
English
2013
1
38
11665
11673
none
Trifiletti, V., Ruffo, R., Turrini, C., Tassetti, D., Rocera, R., Di Fonzo, F., et al. (2013). Dye-sensitized solar cells containing plasma jet deposited hierarchically nanostructured TiO2 thin photoanodes. JOURNAL OF MATERIALS CHEMISTRY. A, 1(38), 11665-11673 [10.1039/c3ta11485f].
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/47060
Citazioni
  • Scopus 23
  • ???jsp.display-item.citation.isi??? 16
Social impact