Abstract: Earth-abundant and non-toxic Kesterite-based Cu2ZnSnS4 (CZTS) thin film solar cells are successfully fabricated on flexible Molybdenum (Mo) foil substrates by an electrodeposition-annealing route. A well-adherent, densely packed, homogeneous, compact, and mirror-like CZT precursor is initially produced through electrodeposition by using a rotating working electrode. Subsequently, the co-electrodeposited CuZnSn (CZT) precursor is sulfurized in quartz tube furnace at 550 °C for 2 h in N2 atmosphere with the presence of elemental sulfur in order to form CZTS. Different characterization techniques like XRD, SEM, HR-TEM, Raman, and Photoluminescence demonstrate that almost phase-pure CZTS formed after sulfurization. A flexible Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil solar cell is produced, where CdS is deposited by chemical bath deposition and transparent conducting oxide (TCO) is deposited by DC sputtering. The CZTS solar device shows a 0.55% power conversion efficiency on flexible Mo foil substrate and it constitutes the first prototype of this kind of solar cell produced by electrodeposition-annealing route without any surface modification of the Mo substrate. Graphic abstract: [Figure not available: see fulltext.].
Khalil, M., Bernasconi, R., Lucotti, A., Le Donne, A., Mereu, R., Binetti, S., et al. (2021). CZTS thin film solar cells on flexible Molybdenum foil by electrodeposition-annealing route. JOURNAL OF APPLIED ELECTROCHEMISTRY, 51(2), 209-218 [10.1007/s10800-020-01494-1].
CZTS thin film solar cells on flexible Molybdenum foil by electrodeposition-annealing route
Le Donne A.;Mereu R. A.;Binetti S.;
2021
Abstract
Abstract: Earth-abundant and non-toxic Kesterite-based Cu2ZnSnS4 (CZTS) thin film solar cells are successfully fabricated on flexible Molybdenum (Mo) foil substrates by an electrodeposition-annealing route. A well-adherent, densely packed, homogeneous, compact, and mirror-like CZT precursor is initially produced through electrodeposition by using a rotating working electrode. Subsequently, the co-electrodeposited CuZnSn (CZT) precursor is sulfurized in quartz tube furnace at 550 °C for 2 h in N2 atmosphere with the presence of elemental sulfur in order to form CZTS. Different characterization techniques like XRD, SEM, HR-TEM, Raman, and Photoluminescence demonstrate that almost phase-pure CZTS formed after sulfurization. A flexible Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil solar cell is produced, where CdS is deposited by chemical bath deposition and transparent conducting oxide (TCO) is deposited by DC sputtering. The CZTS solar device shows a 0.55% power conversion efficiency on flexible Mo foil substrate and it constitutes the first prototype of this kind of solar cell produced by electrodeposition-annealing route without any surface modification of the Mo substrate. Graphic abstract: [Figure not available: see fulltext.].
| File | Dimensione | Formato | |
|---|---|---|---|
|
10281-305201_VoR.pdf
accesso aperto
Tipologia di allegato:
Publisher’s Version (Version of Record, VoR)
Licenza:
Creative Commons
Dimensione
1.31 MB
Formato
Adobe PDF
|
1.31 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.